3D4Makers PCL 90 750g 1.75mm/2.85mm
  • 3D4Makers PCL 90 750g 1.75mm/2.85mm

3D4Makers PCL Ortho 750g

Facilan Ortho is a high-performance 3D printing filament developed specifically for orthotics applications. 

Tax excluded
In stock. Dispatch within 48 hours.

Compare now

Polycaprolactone (PCL) is a high quality biodegradable plastic derived from petrochemical feedstock which is compostable under home composting conditions. PCL is a polyester that is semi-crystalline leading to a clean white final appearance, the product can be coloured easily. The density of PCL is around 1.2kg/cm3 and it has exceptional mechanical properties. PCL melts around 60°C which makes it a safe thermoplastic to print. And with a glass transition temperature of -60°C the product is extremely flexible and tough.

The unique properties of the 3D4Makers PCL Filament make it particularly suitable for usage in FDM and FFF 3D printers. The material has an excellent adhesion between layers which results in great improvement of the impact resistance, strength, durability and the printing process. Due to the low melting point of PCL it can be re-shaped after 3D printing with water of 55 °C.

The PCL Filament produced by3D4Makers is in compliance with the European regulations EC No. 1935/2004 and EC No. 10/2011 concerning plastic materials and articles coming into contact with food. The colorants used by 3D4Makers to colour the Filament also meet these European regulations.

The moleclar weight according ASTM of our PCL is:

Mn GPC, THF, 25 dg celsius 47500 +/- 2000
Mw GPC, THF, 25 dg celsius 84500 +/- 1000
Mz GPC, THF, 25 gd celsius 130000 +/- 5000

Polydispersity ( Mw/Mn) 1,78

CAS Number 24980-41-4

Purity > 99%

Recommended restrictions

Do not use in medical applications involving permanent implantation in the human body. The PCL Filament produced by 3D4MAKERS meets the European RoHS and REACH guidelines.


Data sheet

Printing Temperature
115 - 145°C
Bed Temperature
30 - 45°C
BuildTak, Glass with glue, DimaFix

Specific References