Apium CFR PEEK black 1.75mm
  • Apium CFR PEEK black 1.75mm
  • Apium CFR PEEK black 1.75mm
  • Apium CFR PEEK black 1.75mm 500g

Apium CFR PEEK black 1.75mm 500g

Carbon Fiber Reinforced PEEK from Apium, is a material formulated with Carbon Fibres and PEEK. Its high thermal conductivity, enabled thanks to its specific formulation, made CFR PEEK an ideal material for a variety of industries as aerospace or electronic. Create functional prototyping, end-use parts or material development with the CFR PEEK material.

$569.00
Tax excluded
Quantity
Last items in stock

Compare now


Adavanced materials for advanced projects.

With the continued cooperation and commitment to providing the highest quality of material, Apium guarantees the purity and dimensional tolerances of all their materials. They focus and develop high-performing materials to fulfil their suitability for FFF 3D printing technology always. 
 

Apium CFR PEEK Black Material:

For the production of lightweight or high thermal conductivity parts, Apium CFR PEEK filament enables the 3D print of models from prototypes to end-use parts. This material is a combination of Carbon Fibers and PEEK which makes possible the print of parts where thermal management is particularly important. Thanks to its different properties, CFR PEEK is suitable for the print of part as drive shafts, electrical insulators, heats dissipation and much more.

Applications:
 Aerospace, Automotive, Electronic, Oil & Gas


Key Features:

  • High wear resistance
  • Low density 
  • Good chemical resistance
  • Excellent tensile strength
  • Hydrolysis and superheated steam resistant
  • High stiffness
  • Long -term temperature capabilities
  • Corrosion resistance
  • Stable performance









APM00005
1 Item

Data sheet

Filament Diameter (mm)
1.75
Colour
Opaque Black
Weight
500g
Material
Polyetheretherketone with carbon fibre fillers
Melting Temperature
341˚C
Tensile Strength
112 MPa
Tensile Modulus
6000 MPa
Compressive Strength
25/47 MPa
Shore D hardness
298
Tensile Elongation
10%