    Anisoprint - Smooth PA - 750g

    Smooth PA is a carbon fiber-filled polyamide filament by Anisoprint. Smooth PA is used specifically for the exterior of a part to create a stronger shell and display a matte look with a sleek surface.

    130,00 €
    TTC
    Quantité
    Rupture de stock

     

    Assistance à distance gratuite à vie sur tous les produits

     

    Demandez nous un devis pour les promotion liées au secteur de l'éducation

    Anisoprint’s Smooth PA is easy-to-use and guarantees a flawless surface quality. Specifically designed in collaboration with experienced filaments manufacturer Polymaker for use with the Anisoprint Composer A4/A3 and IS Prom printers, Smooth PA is a carbon fibre/polyamide blend for printing tougher, durable, functional parts while offering low moisture absorption as well as anti-warping properties.

    Printing Guidelines

    • Temperature: best printed between 250 and 270°C
    • Speed : recommended between 40-50mm/s for standard Composer A4/A3 setup
    • Buildplate adhesion: required to be between 55-60°C
    • Drying and storage: Possibility to be printed from open air with no significant damage. Longer prints require the use of a dryer at 60°C and storage in a dry area such as a sealed box with silica gel
    • Nozzles: abrasion-resistant nozzle such as the Composer Hardened steel nozzle (0.4 or 0.6) is required.

    anisoprint desktop logo


    For further information and advice on how Anisoprint can benefit your business, please do not hesitate to get in touch with one of our advisors by calling the telephone number at the top of the page, or by clicking the button below and requesting a call-back:

    Contactez un conseiller

    Anisoprint

    Tensile Strength
    71.63±1.67 (100° ANNEALED)
    Flexural Strength
    109.97±1.38 (100° ANNEALED)
    Flexural Modulus
    3535.0±239.29 (100° ANNEALED)
    Young’s Modulus (MPa)
    3304.39±145.15 (100° ANNEALED)
    Elongation at Break (%)
    3.57±0.25 (100° ANNEALED)