LOCTITE 3D | IND147 HDT230 High Heat

    The Henkel LOCTITE 3D IND147 HDT230 High Heat is a durable resin, created for the use in tooling and molding applications. This material is very heat resistant. The LOCTITE 3D IND147 HDT230 is available in black.

    $260.00
    Tax excluded
    Size
    Quantity
    Available to order.

     

    Free shipping on orders over $500 to mainland US

     

    Free lifetime remote support on all products

    Henkel Loctite Logo

    The LOCTITE 3D IND147 HDT230 High Heat

    The IND147 HDT230 is a tough resin with high temperature resistance, perfect for tooling and molding applications. The material is stable with a great surface finish and can withstand mechanical stresses.

    Key Features

    • High Heat Deflection Temperature
    • Tough with goos dimensional stability
    • Good surface finish
    Mechanical PropertiesMethodGreenDymax 5000 (10 min. per side)Dymax 5000 (10 min. per side) 170°C for 3 hours
    Tensile Stress at BreakASTM D63830.7 ± 1.6 MPa75 ± 2.0 MPa84 ± 4.7 MPa
    Young's ModulusASTM D6381150 ± 137 MPa3192 ± 35MPa3285 ± 131MPa
    Elongation at FailureASTM D6385.9 ± 1.7 %3.0 ± 0.1 %3.2 ± 0.3 %
    Flexural Stress at YieldASTM D79068 ± 3 MPa130 ± 11 MPa126 ± 11 MPa
    Flexural ModulusASTM D7902053 ± 1893835 ± 131 MPa3926 ± 51 MPa
    Flexural Strain at BreakASTM D7907.6 ± 2.7 %3.1 ± 0.4 %3.2 ± 0.3 %
    Thermal PropertiesMethodGreenDymax 5000 (10 min. per side)Dymax 5000 (10 min. per side) 170°C for 3 hours
    HDT at 0.455 MPa DMAInternal56.1° C140° C237° C
    HDT at 1.82 MPa DMAInternal111° C166.7° C
    HDT at 0.455 MPa VICATASTM D648230.6° C
    HDT at 1.82 MPa VICATASTM D648
    Coefficient of Thermal Expansion (25 - 200° C)ASTM E831114μm/m-°C106μm/m-°C
    Other PropertiesMethodGreenDymax 5000 (10 min. per side)Dymax 5000 (10 min. per side) 170°C for 3 hours
    Durometer (Shore D, 0 sec)ASTM D224094D94.5D
    IZOD Impact StrengthASTM D25614.6 J/m14.5 J/m
    Water Absorption (24 hr)ASTM D5700.25 %
    Solid DensityASTM D7921.246 g/cm³1.262 g/cm³
    Shrinkage by DensityASTM D7928.25 %9.64 %
    Liquid PropertiesMethodGreenDymax 5000 (10 min. per side)Dymax 5000 (10 min. per side) 170°C for 3 hours
    Viscosity at 25° CASTM D78672105 ± 200 cP
    Liquid DensityASTM D14751.15 g/mL

    Data sheet

    Young’s Modulus (MPa)
    30.7 ± 1.6 MPa